FRP Touring Car
|
Features and main uses:
|
|
The resin is suitable for FRP products with mechanical strength and toughness and FRP coil plate. It has low viscosity, high strength, good toughness and good wettability to glass fiber.
|
|
Technical index of liquid resin（25℃）:
|
|
Project
|
Company
|
Index
|
Test Method
|
|
Appearance
|
...
|
Light yellow liquid
|
...
|
|
Viscosity
|
Pa?s
|
0.15~0.2
|
GB/T7193.4.1
|
|
Gel time
|
min
|
5.0~6.0
|
GB/T7193.4.6
|
|
Note: gel time test:Resin 100g；Accelerator 1.0%Co 2.0g；Curing agent Butanox M-50 1.0g
|
|
|
|
Physical properties of casting body:
|
|
Project
|
Company
|
Measured value
|
Test Method
|
|
Tensile strength
|
MPa
|
73
|
GB/T2567-2008
|
|
Tensile modulus of elasticity
|
MPa
|
3348
|
GB/T2567-2008
|
|
Breaking extensibility
|
...
|
4.11%
|
GB/T2567-2008
|
|
Bending strength
|
MPa
|
121
|
GB/T2567-2008
|
|
Bending modulus of elasticity
|
MPa
|
3247
|
GB/T2567-2008
|
|
Hot deformation temperature
|
℃
|
73
|
GB/T1634-2004
|
|
Barcol hardness
|
...
|
44
|
GB/T3854-2005
|
|
Note: 1. The preparation method is in accordance with GB / T8237-2005, curing system: Accelerator RCA 1.0%, Curing agent Butanox M-50 1.0%.
|
|
2. Casting body post-treatment: room temperature×24 hours + 60 ℃×3 hours + 90 ℃×1 hours.
|
|
|
|
Matters needing attention:
|
|
1. When the construction environment temperature is high and the gel time is short, the dosage of curing agent can not be reduced, and the inhibitor should be added as needed. When the surface is sticky, proper wax solution should be added.
|
|
2. The product should be stored in a cool place below 25 ℃ to avoid fire and keep away from heat and radiation sources. The shelf life of products stored below 25 ℃ is 3 months.
|
|
|
|
In view of the diversity of application conditions, it is necessary for users to confirm the product performance. If you have any questions about the contents of this information or want to know more information, please contact our company. We reserve the right to modify the data.
|