HK-199
|
Features and main uses：
|
|
M-benzene type heat-resistant and chemical resistant unsaturated polyester resin. The FRP products can withstand 200 ℃ high temperature. It is suitable for manufacturing chemical equipment and FRP products with high heat resistance requirements.
|
|
Technical index of liquid resin（25℃）:
|
|
Project
|
Company
|
Index
|
Test Method
|
|
Appearance
|
...
|
Light yellow transparent liquid
|
...
|
|
Viscosity
|
Pa?s
|
0.42~0.78
|
GB/T7193.4.1
|
|
Acid value
|
mgKOH/g
|
17.0~24.0
|
GB/T2895
|
|
Gel time
|
min
|
10.0~20.0
|
GB/T7193.4.6
|
|
Note: gel time test:CH50 2%
|
|
|
|
Physical properties of casting body:
|
|
Project
|
Company
|
Measured value
|
Test Method
|
|
Tensile strength
|
MPa
|
64
|
GB/T2567-2008
|
|
Tensile modulus of elasticity
|
MPa
|
3232
|
GB/T2567-2008
|
|
Breaking extensibility
|
...
|
2.73%
|
GB/T2567-2008
|
|
Bending strength
|
MPa
|
105
|
GB/T2567-2008
|
|
Bending modulus of elasticity
|
MPa
|
3348
|
GB/T2567-2008
|
|
Impact strength
|
KJ/M2
|
7.4
|
GB/T2567-2008
|
|
Hot deformation temperature
|
℃
|
122
|
GB/T1634-2004
|
|
Oxygen index
|
...
|
45%
|
GB/T8924-2005
|
|
Note: 1. The preparation method is in accordance with GB / T8237-2005，Curing system: Accelerator RCA 1.0%, curing agent Butanox M-50 1.0%.
|
|
2. Casting body post-treatment: room temperature×24 hours + 60 ℃×3 hours + 120 ℃×1 hours.
|
|
|
|
Matters needing attention:
|
|
1. When the construction environment is high and the gel time is too short, the dosage of curing agent can not be reduced, and the polymerization inhibitor should be added as needed. When the surface is sticky, wax fluid should be added properly.
|
|
2. The product should be stored in a cool place below 25 ℃ to avoid fire and keep away from heat and radiation sources. The shelf life of products stored below 25 ℃ is 3 months.
|
|
|
|
In view of the diversity of application conditions, it is necessary for users to confirm the product performance. If you have any questions about the contents of this information or want to know more information, please contact our company. We reserve the right to modify the data.
|