TM-196FRP
|
Features and main uses：
|
|
TM-196FRP is a kind of waxy unsaturated polyester resin with medium viscosity. It has good wettability to glass fiber. Its FRP products have good toughness and mechanical strength. It is suitable for hand lay up of vehicle shell, vehicle parts and other glass products.
|
|
Technical index of liquid resin（25℃）:
|
|
Project
|
Company
|
Index
|
Test Method
|
|
Appearance
|
...
|
Transparent yellow liquid
|
...
|
|
Viscosity
|
Pa?s
|
0.7~1.1
|
GB/T7193.4.1
|
|
Gel time
|
min
|
14.0~22.0
|
GB/T7193.4.6
|
|
|
|
Physical properties of casting body:
|
|
Project
|
Company
|
Measured value
|
Test Method
|
|
Tensile strength
|
MPa
|
70.0
|
GB/T2567-2008
|
|
Tensile modulus of elasticity
|
MPa
|
3700.0
|
GB/T2567-2008
|
|
Breaking extensibility
|
...
|
2.50%
|
GB/T2567-2008
|
|
Bending strength
|
MPa
|
130.0
|
GB/T2567-2008
|
|
Bending modulus of elasticity
|
MPa
|
3800.0
|
GB/T2567-2008
|
|
Impact strength
|
KJ/m2
|
12.0
|
GB/T2567-2008
|
|
Hot deformation temperature
|
℃
|
76
|
GB/T1634-2004
|
|
Barcol hardness
|
...
|
48
|
GB/T3854-2005
|
|
Note: 1. The preparation method is in accordance with GB / T8237-2005, curing system: Accelerator RCA 1.2%, curing agent Butanox M-50 2.0%.
|
|
2. Casting body post-treatment: room temperature×24 hours + 60 ℃×3 hours + 90 ℃×1 hours.
|
|
|
|
Reference formula:
|
|
TM-196FRP resin 100 copies；Curing agent （MEKPO） 1 ~ 2 copies (dosage depends on temperature)；Accelerator RCA 1~4 copies(dosage depends on temperature)
|
|
|
|
Matters needing attention:
|
|
The product should be stored in a cool place below 25 ℃ to avoid fire and keep away from heat and radiation sources. The shelf life of products stored below 25 ℃ is 3 months.
|
|
|
|
In view of the diversity of application conditions, it is necessary for users to confirm the product performance. If you have any questions about the contents of this information or want to know more information, please contact our company. We reserve the right to modify the data.
|