FH-H-1070(N)HC
|
Features and main uses：
|
|
FH-H-1070 is a kind of o-phenylene unsaturated polyester resin with low and medium viscosity. Its FRP products have good mechanical strength and high elongation, which is suitable for hand lay up ordinary FRP products.
|
|
Technical index of liquid resin:
|
|
Project
|
Company
|
FH-H-1070(N)WHC
|
FH-H-1070(N)MHC
|
FH-H-1070(N)SHC
|
Test Method
|
|
Appearance
|
...
|
Purplish liquid
|
...
|
|
Viscosity（25℃）
|
Pa?s
|
0.22~0.32
|
0.3~0.45
|
0.3~0.45
|
JIS K 6901.5.6
|
|
Thixotropy index
|
...
|
≥1.2
|
JIS K 6901.5.6
|
|
Gel time（25℃）
|
min
|
10.0~18.0
|
20.0~30.0
|
30.0~40.0
|
JIS K 6901.5.10
|
|
Note: Gel time test:Curing agent Butanox M-50 2.0%
|
|
|
|
Physical properties of casting body:
|
|
Project
|
Company
|
Measured value
|
Test Method
|
|
|
Tensile strength
|
MPa
|
65.0
|
GB/T2567-2008
|
|
Breaking extensibility
|
...
|
3.70%
|
GB/T2567-2008
|
|
Bending strength
|
MPa
|
112.0
|
GB/T2567-2008
|
|
Impact strength
|
KJ/m2
|
10.3
|
GB/T2567-2008
|
|
Hot deformation temperature
|
℃
|
70
|
GB/T1634-2004
|
|
Barcol hardness
|
...
|
42
|
GB/T3854-2005
|
|
Note: 1. Dosage of curing agent:Butanox M-50 1.0%
|
|
2.Casting body: 3 mm thick, post curing: room temperature×24 hours + 60 ℃×3 hours + 80 ℃×1 hours.
|
|
|
|
Matters needing attention:
|
|
1. Before use, please mix evenly in the packaging barrel, or pour out all the resin in the packaging barrel and stir it evenly before use.
|
|
2. When the construction environment humidity is high or the temperature is high, it is easy to cause surface stickiness. At this time, rs-102 wax can be properly added, and the recommended addition amount is 0.4 ~ 0.8%.
|
|
3. The product should be stored in a cool place below 25 ℃ to avoid fire and keep away from heat and radiation sources. The shelf life of products stored below 25 ℃ is 3 months.
|
|
|
|
In view of the diversity of application conditions, it is necessary for users to confirm the product performance. If you have any questions about the contents of this information or want to know more information, please contact our company. We reserve the right to modify the data.
|