TP-156
|
Features and main uses:
|
|
TP-156 is used to produce translucent, three-dimensional artificial marble / agate products, such as wash and make-up table, kitchen table panel, bathtub, etc. It has good curing property, short molding cycle, high thermal deformation temperature and small warpage.
|
|
Technical index of liquid resin（25℃）:
|
|
Project
|
Company
|
Index
|
Test Method
|
|
Appearance
|
...
|
Lavender liquid
|
...
|
|
Viscosity
|
Pa?s
|
1.3~1.7
|
B-54953
|
|
Gel time
|
min
|
8.0~16.0
|
C-82801
|
|
Chroma
|
...
|
Less than 60
|
HR-B-42300
|
|
Note: gel time test:AKZO M-50 1.0%
|
|
|
|
Physical properties of casting body:
|
|
Project
|
Company
|
Measured value
|
Test Method
|
|
Tensile strength
|
MPa
|
66
|
GB/T2568-95
|
|
Tensile modulus of elasticity
|
MPa
|
4060
|
GB/T2568-95
|
|
Breaking extensibility
|
...
|
1.70%
|
GB/T2568-95
|
|
Bending strength
|
MPa
|
108
|
GB/T2570-95
|
|
Bending modulus of elasticity
|
MPa
|
3900
|
GB/T2570-95
|
|
Hot deformation temperature
|
℃
|
90
|
GB/T1634-89
|
|
Impact strength
|
KJ/M2
|
1.7
|
GB/T2571-95
|
|
Barcol hardness
|
...
|
47
|
GB/T3854-83
|
|
Water absorption
|
25℃，24h，%
|
0.3
|
GB/T1462-88
|
|
Note: 1. The preparation method is in accordance with GB / T8237-2005, curing system: Curing agent Butanox M-50 1.0%.
|
|
2. Casting body post-treatment: 60 ℃×3 hours + 110 ℃×1 hours.
|
|
|
|
Matters needing attention:
|
|
1. When the construction temperature is high and gel time is short, the dosage of curing agent can not be less than 1%, and gel retardants RS-406 should be added as needed.
|
|
2. The product should be stored in a cool place below 25 ℃ to avoid fire and keep away from heat and radiation sources. The shelf life of products stored below 25 ℃ is 3 months.
|
|
|
|
In view of the diversity of application conditions, it is necessary for users to confirm the product performance. If you have any questions about the contents of this information or want to know more information, please contact our company. We reserve the right to modify the data.
|
http://m.xxzxmr.com/en/chanpinzhongxin_v306.html