CN-H-1005
|
Features and main uses：
|
|
CN-H-1005 is a putty resin for automobile repair. It has good air drying and flexibility, short grinding time and good storage stability.
|
|
Technical index of liquid resin（25℃）:
|
|
Project
|
Company
|
Index
|
Test Method
|
|
Appearance
|
...
|
Yellow transparent liquid
|
...
|
|
Viscosity
|
Pa?s
|
0.18~0.33
|
GB/T7193.1
|
|
Solid content
|
...
|
(59.0~65.0)%
|
B-22301
|
|
Gel time
|
min
|
6.0~12.0
|
JIS K 6901.4.8
|
|
Note: gel time test:6.0%Co-Naph 1.0%；AKZO M-50 2.0%
|
|
|
|
Physical properties of casting body:
|
|
Project
|
Company
|
Measured value
|
Test Method
|
|
Tensile strength
|
MPa
|
35.3
|
GB/T2568-95
|
|
Tensile modulus of elasticity
|
MPa
|
1760
|
GB/T2568-95
|
|
Breaking extensibility
|
...
|
12.50%
|
GB/T2568-95
|
|
Bending strength
|
MPa
|
66.1
|
GB/T2570-95
|
|
Bending modulus of elasticity
|
MPa
|
1760
|
GB/T2570-95
|
|
Barcol hardness
|
...
|
24
|
GB/T3854-83
|
|
Note: 1. The preparation method is in accordance with GB / T8237-2005
|
|
2. Casting body post-treatment:60 ℃×3 hours + 110 ℃×1 hours.
|
|
|
|
Matters needing attention:
|
|
1. When the construction environment temperature is high and gel time is short, the dosage of curing agent can not be reduced, and gel retarding agent RS-104 should be added as needed.
|
|
2. The product should be stored in a cool place below 25 ℃ to avoid fire and keep away from heat and radiation sources. The shelf life of products stored below 25 ℃ is 3 months.
|
|
|
|
In view of the diversity of application conditions, it is necessary for users to confirm the product performance. If you have any questions about the contents of this information or want to know more information, please contact our company. We reserve the right to modify the data.
|