FH-286
|
Features and main uses:
|
|
FH-286 belongs to the UP-HE resin of JIS-K-6919. With excellent hot water resistance, thixotropic agent and accelerant have been added. It is suitable for hand lay up process.It can be used to make FRP bathtub heat-resistant interlayer or other hot-water-resistant FRP products.
|
|
Technical index of liquid resin（25℃）:
|
|
Project
|
Company
|
Index
|
Test Method
|
|
Appearance
|
...
|
No abnormality
|
...
|
|
Viscosity
|
Pa?s
|
0.2~0.4
|
JIS-K-6901.4.5
|
|
Thixotropy index
|
...
|
1.4~3.0
|
JIS-K-6901.4.5
|
|
Gel time
|
min
|
8.0~22.0
|
JIS-K-6901.4.8
|
|
Note:Gel time test：Curing agent Butanox M-50 1.0%
|
|
|
|
Physical properties of casting body:
|
|
Project
|
Company
|
Measured value
|
Test Method
|
|
Tensile strength
|
MPa
|
5.8
|
JIS-K-7113
|
|
Tensile modulus of elasticity
|
MPa
|
400
|
JIS-K-7113
|
|
Breaking extensibility
|
...
|
1.60%
|
JIS-K-7113
|
|
Bending strength
|
MPa
|
11
|
JIS-K-7203
|
|
Bending modulus of elasticity
|
MPa
|
390
|
JIS-K-7203
|
|
Impact strength
|
KJ/M2
|
1.9
|
JIS-K-7111
|
|
Hot deformation temperature
|
℃
|
100
|
JIS-K-7207
|
|
Barcol hardness
|
...
|
43
|
JIS-K-7060
|
|
Water absorption
|
%
|
0.22
|
JIS-K-7209
|
|
Note: 1. The preparation method is in accordance with GB / T8237-2005, curing system:Curing agent Butanox M-50 1.0%
|
|
2. Casting body post-treatment:110 ℃×2 hours.
|
|
|
|
Matters needing attention:
|
|
The product should be stored in a cool place below 25 ℃ to avoid fire and keep away from heat and radiation sources. The shelf life of products stored below 25 ℃ is 3 months.
|
|
|
|
In view of the diversity of application conditions, it is necessary for users to confirm the product performance. If you have any questions about the contents of this information or want to know more information, please contact our company. We reserve the right to modify the data.
|