HK-806
|
Features and main uses：
|
|
It is suitable for SMC and BMC moulded automobile parts, electrical switches, insulators, plastic packaging and other products with high performance requirements.
|
|
Technical index of liquid resi（25℃）:
|
|
Project
|
Company
|
Index
|
Test Method
|
|
Appearance
|
...
|
Light yellow transparent liquid
|
...
|
|
Viscosity
|
Pa?s
|
1.5~2.0
|
GB/T7193.4.1
|
|
Acid value
|
mgKOH/g
|
18.0~25.0
|
GB/T2895
|
|
Gel time
|
min
|
4.0~7.5
|
GB/T7193.4.6
|
|
Note: gel time test: CH50 2%
|
|
|
|
Physical properties of casting body:
|
|
Project
|
Company
|
Measured value
|
Test Method
|
|
Tensile strength
|
MPa
|
48.8
|
GB/T2567-2008
|
|
Tensile modulus of elasticity
|
MPa
|
3430
|
GB/T2567-2008
|
|
Breaking extensibility
|
...
|
1.58%
|
GB/T2567-2008
|
|
Bending strength
|
MPa
|
80.6
|
GB/T2567-2008
|
|
Bending modulus of elasticity
|
MPa
|
4010
|
GB/T2567-2008
|
|
Impact strength
|
KJ/m2
|
5.0
|
GB/T2567-2008
|
|
Hot deformation temperature
|
℃
|
120
|
GB/T1634-2004
|
|
Barcol hardness
|
...
|
48
|
GB/T3854-2005
|
|
Note: 1. The preparation method is in accordance with GB / T8237-2005, curing system: Accelerator RCA 1.0%, curing agent Butanox M-50 1.0%.
|
|
2. Casting body post-treatment: room temperature×24 hours + 60 ℃×3 hours + 120 ℃×1 hours.
|
|
|
|
Matters needing attention:
|
|
1. Due to the high temperature in summer, please add proper amount of polymerization inhibitor to ensure the storage stability of SMC / BMC.
|
|
2. The product should be stored in a cool place below 25 ℃ to avoid fire and keep away from heat and radiation sources. The shelf life of products stored below 25 ℃ is 3 months.
|
|
|
|
In view of the diversity of application conditions, it is necessary for users to confirm the product performance. If you have any questions about the contents of this information or want to know more information, please contact our company. We reserve the right to modify the data.
|